Effect of Mid Plane Layer on Flexural Properties of Plies Under Transverse Loading | ||
| Albahir journal | ||
| Article 1, Volume 2, Issue 3, 2015, Pages 15-19 | ||
| Authors | ||
| Harith Ibrahim Jaffer; Zainab Raheem Muslem | ||
| Abstract | ||
| Abstract The effect of mid layer on flexural strength and young modulus were studied using Instron testing machine. E-glass/epoxy composites were manufactured using hand lay-up technique. The laminated composites were prepared with dimension (4x10x80) mm, Epoxy composites were reinforced with multidirectional layer of woven glass fiber and random glass fiber of stacking sequence [M]16, [R]16, [M/R//M1/M1//R/M]s, [//M/R//]s, and [R/M//R1/R1//M/R]s. The effect of transverse loading on flexural strength and young modulus was investigated for specimens subjected to Three-point bending test. The results show that the mid layer (M1/M1) which had (homogeneous distribution) has higher flexural strength value and young modulus than mid layer (M1/R1) and (R1/R1). | ||
| Keywords | ||
| mid plane; exural Properties; transverse loading | ||
|