Effect of Micro Powder on Mechanical and Physical Properties of Glass Fiber Reinforced Epoxy Composite | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 34, 7A, 2016, Pages 1402-1414 PDF (1.15 M) | ||
| DOI: 10.30684/etj.34.7A.12 | ||
| Authors | ||
| Aseel Basim Abdul-Hussein; Fadhel Abbas Hashim; Tamara Raad Kadhim | ||
| Abstract | ||
| In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as the matrix, 3% volume fractions of Glass Fibers (G.F) as re enforcement and 2%, 4%, 6% volume fraction of micro powder (Aluminum Oxide Al2O3, Silicon Oxide SiO2 and Titanium Oxide TiO2) as filler. Studied the, hardness test, flexural strength, density, water absorption measurements and tests were conducted to reveal their values for each type of composite material. The results showed that the non – reinforced epoxy have lower properties than nano composites material. Measured density results had show an incremental increase with volume fraction increase and water absorption, hardness, and flexural strength had show an incremental increase with volume fraction increase and with smaller particle size. | ||
| Keywords | ||
| Density; Water absorption; Hardness; flexural strength; Glass Fibers; composites | ||
|