Fatigue Performance of 2017-T4 AL. alloy Under sub-zero Temperature by Using Electromechanical Freezing System | ||
| Engineering and Technology Journal | ||
| Article 8, Volume 34, 14A, 2016, Pages 2631-2641 PDF (737.68 K) | ||
| DOI: 10.30684/etj.34.14A.8 | ||
| Authors | ||
| Hussain J.M. Alalkawi; Fikrat Abdulkareem Fattah; Duaa Amer Kadhim | ||
| Abstract | ||
| The effects of sub-zero(-22Co) cyclic rotating bending on the S-N behavior and cumulative damage are reported for 207-T4 aluminum alloy .Experimental characterization of fatigue behavior showed that the S-N curves behavior may described by the following Basquin's formulas: σ_f=1230〖(N_f)〗^(-0.15) At room temperature (RT) And σ_f=1563〖(N_f)〗^(-0.17) At sub-zero temperature (-22Co) From the above equation, the fatigue behavior can be change at σ_f=204 MPa and N_f=159475 cycles . Slightly increase in fatigue life results above 204 MPa and slightly decrease in fatigue below the 204 MPa stress level. A non-linear experimental law is introduced for the accumulation of damage at sub-zero temperature variable fatigue. This law gave conservative and safe fatigue life time prediction when applying to the data of variable fatigue at low temperature (-22 Co). | ||
| Keywords | ||
| Fatigue behavior at sub; zero temperature; cumulative fatigue damage; Al alloy | ||
|