Mechanical And Physical Properties oF a Hybrid Composite With Basis oF Aluminum

N. Razooqi, Raed

	Mechanical And Physical Properties oF a Hybrid Composite With Basis oF Aluminum
Tikrit Journal of Pure Science
Article 1, Volume 22, Issue 5, 2017, Pages 148-155
Author
Raed N. Razooqi
Abstract
This research inculdes using a powder metallurgy technique (PM) to manufacture composites with a basis of (99.7%) purity of Aluminum, and by adopting a volumetric ratios via adding both copper with purity and Graphite with (99.8%) purity as reinforced materials. The Copper is added in a constant ratio and with different ratios (0, 3, 6, 9, 12) and (15%). The pressing process was in one way with a pressure of (700-MPa).for forming. This research studied effect of the reinforcing on the physical and mechanical properties of composites after sintering them with a temperature of (600◦C) for two hours by an oven with a heat rate of (4◦C/min). The results show that the Graphite content is inversely proportional with the volumetric and apparent density and the thermal conductivity when the composite F (Al+4%Cu) got high properties. Furthermore , both composites F and A had the same behavior for mechanical properties such as hardness and radial compression strength . In addition , the total porosity and the ability of water absorption was increase with Graphite ratio in composites, as example the ability of water absorption increased by (0.61%) for composite B (Al+4%Cu+3%Gr) Compared with composite F.
Keywords
Powder metallurgy technique; Reinforcing; Hybrid composite; Physical Properties; mechanical properties

Statistics Article View: 116 PDF Download: 96