Effect of High Temperature on Compressive Strength of StructuralLightweight and Normal Weight Concretes | ||
| Iraqi Journal of Civil Engineering | ||
| Article 9, Volume 6, Issue 1, 2009, Pages 59-74 PDF (116.86 K) | ||
| DOI: 10.37650/ijce.2009.14193 | ||
| Author | ||
| Mahmoud Kh. Mohammed | ||
| Abstract | ||
| Abstract:This research studies the effect of high temperature which is reached to 600 °C onstructural lightweight and normal weight concrete. Lightweight concrete mix designedaccording to ACI committee 211-2-82 with mix proportion 1:1.12 :3.35 by volume .Thewc ratio equal to 0.5 by weight and cement content 550 kgm3. Mix proportions ofnormal weight concrete were 1:2:3 by weight with cement content 400 kgm3 and samewc. The design compressive strength at 28 days of normal weight concrete (NWC) andlightweight concrete (LWC) were 34.7 MPa and 22.62 MPa respectively. Compressivestrength tests were performed on 100 mm cubes exposed to high temperature 100,200,400and 600 °C. The normal weight concrete and light weight concrete test specimens wereexposed to high temperature for 10 minute suddenly at the required degree. Moreover,light weight concrete test specimens tested after graduate exposure to high temperaturereaching to the required degree with and without drying to examine the effect of moisturecontent.The results indicated that the structural lightweight concrete exhibits approximatelysimilar compressive strength loss compared to normal weight concrete up to 600 °C at 28days in graduate exposure .The percentage of reduction on compressive strength was30% in lightweight concrete compared to 28% in normal weight concrete at 600 °C .Insudden exposure to high temperature ,the opposite behavior was noticed .The percentageof reduction on compressive strength was 64.4% in lightweight concrete at 600°C .Drying of lightweight concrete specimens before graduate exposure to high temperaturessignificantly reduce the loss of compressive strength. | ||
|