Investigation the Creep-Fatigue Behavior and A.C. Electrical Conductivity of AA 6061 Under Ultrasonic Peening | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 37, 11A, 2019, Pages 453-459 PDF (788.4 K) | ||
| Document Type: Research Paper | ||
| DOI: 10.30684/etj.37.11A.1 | ||
| Authors | ||
| Hussain J. Al-Alkawi; Ahmed H. Reja; Mahmood F. Abbas | ||
| Electromechanical Engineering Department, University of Technology - Iraq | ||
| Abstract | ||
| Ultrasonic peening is an innovative surface improvement process used to increase the resistance of aircraft metals and enhance high cycle fatigue life. The process creates residual compressive stresses deep into part surfaces. These compressive surface stresses inhibit the initiation and propagation of fatigue cracks. Aluminum alloys are relatively new materials used in aerospace, marine, automobile, and bridges due to low weight, which has significant advantages compared to the other materials. A major concern in the design of Aluminum alloys subjected to variable loads is fatigue strength and life. In this paper mechanical properties, fatigue strength, fatigue life and A.C.. electrical conductivity were studied for AA6061-T6 to assess the effects of ultrasonic peening (UP) on mechanical properties, fatigue at room temperature (RT), creep-fatigue (CF) at 250 ͦC and A.C.. electrical conductivity. Test results showed that after UP, the mechanical properties; ultimate tensile strength (UTS) and yield stress (Ys) were noticeably improved. The improvements in UTS and Ys were enhanced by 5.7% and 1.5% respectively while the ductility was reduced from 16.5% to 15.7%. Fatigue strength was enhanced by 8.37% compared to strength at RT. The results of UT before creep-fatigue CF showed increasing in fatigue strength 147 MPa at CF 250 ̊C and improved to153 MPa after applying UP, indicating 4% improvement in strength. The fatigue life was improved after UP for both RT and CF. It was found that the A.C. electrical conductivity increase as the frequency increase for all the cases above. | ||
| Keywords | ||
| Creep-Fatigue; Aluminum Alloy; Ultrasonic Peening; electrical conductivity | ||
| References | ||
|
[1] R.L. Elwin, “Introduction to Aluminum and Aluminum Alloys,” ASM International, Metals Handbook, Tenth Edition, Vol. 2, pp. 3-14, 1990. [2] H.S. Zahra, “The Effect of AL2O3 Nanomaterials on Fatigue Behavior of 7075 Al-alloy,” MSc Thesis, Material Engineering Dept., Univ. of Al-Mustansiriya, Iraq, 2017. [3] Z.M. Elimat, “Study of A.C. Electrical Properties of Aluminum –Epoxy Composites,” Journal of Physics D: Applied Physics, Vol. 41, No. 16, pp. 7, 2008. [4] R. Ramos, N. Ferreira, J.A.M. Ferreira, C. Capela and A.C. Batista, “Improvement in Fatigue Life of Al 7475-T7351 Alloy Specimens by Applying Ultrasonic and Microshot Peening,” International Journal of Fatigue, Vol. 92, Part 1, pp. 87-95, 2016. [5] H.J. Al-Alkawi, H.M. Amer and F.N. Saba, “Enhancement of Cumulative Corrosion-Fatigue Interaction Lives of AA6061-T6 Aluminum Alloy using Impact Peening Process,” JESD, Vol. 21, No. 0, 2017. [6] S.H. Shaker, N.H. Mohsin and M.A. Raad, “Effect of Ultrasonic Peening Technique on Fatigue Life of 6061-T6 Aluminum Alloy,” Al-Qadisiyah Journal for Engineering Sciences, Vol. 10, No. 2, pp. 171-179, 2017. [7] D., M., Vanini and S.A. Sadough, “Corrosion Fatigue Enhancement of Welded Steel Pipes by Ultrasonic Impact Treatment,” materials letters, Vol. 39, pp. 462-466, 2015. [8] D., Chengli, “Low Cycle Fatigue, Creep and Creep-Fatigue Interaction Behavior of a TiAl Alloy at High Temperatures,” Scripta Materialia, Vol. 144, pp. 60-63, 2018. [9] S. Sabah, “The Effect of Aluminum Oxide Nanoparticles on Dielectric Properties of Polyvinyl Alcohol,” Journal of Industrial Engineering Research, Vol. 1, No. 2, pp. 13-16, 2015. [10] T. Bashir, A. Shakoor, E. Ahmed, N.A. Niaz, I. Shahid, S.A. Muhammad and A.M. Mohammad, “Magnetic, Electrical and Thermal Studies of Polypyrrole-Fe2O3 Nanocomposites,” Polymer Science, Series A, Vol. 59, No. 6, pp. 902-908, 2017. [11] M.H. Abdallah, Y. Alramadin, M. Ahmed, A. Zihlif, S. Jawad and A. Alnajjar, “Electrical Characterization of Metal Fiber-Polyester Composite,” Inter. J. of polymeric materials, Vol. 37, pp. 33-42, 1997. [12] J.R. Davis, “Aluminum and Aluminum Alloy,” ASM International, pp. 351- 416, 2001. [13] N.I.I. Mansor, S. Abdullah, A.K. Ariffin and J. Syarif, “A review of The Fatigue Failure Mechanism of Metallic Materials under a Corroded Environment,” Engineering Failure Analysis, Vol. 42, pp. 353-365, 2014. [14] R. Hales, “A Quantitative Metallographic Assessment of Structural Degradation of Type 316 Stainless Steel During Creep-Fatigue,” Fatigue & Fracture of Engineering Materials & Structures, Vol. 3, No. 4, pp. 339-356, 1980. [15] X.L. Yan, X.C. Zhang, S.T. Tu, S.L. Mannan, F.Z. Xuan and Y.C. Lin, “Review of Creep–Fatigue Endurance and Life Prediction of 316 Stainless Steels,” International Journal of Pressure Vessels and Piping, Vol. 126, pp. 17-28, 2015. [16] S.F. Abdul Jabbar, “Shot Peening and FatigueCreep Interaction Under Variable Amplitude Stresses of Different Aluminum alloys,” Ph.D. Thesis, Mechanical Engineering Department, University of Technology, Baghdad, Iraq, 2012. [17] Device manual, 2014. Available: http://www.hzhccs.com [18] E. Statnikov, O.V. Korolkov and V.N. Vityazev, “Physical and Mechanism of Ultrasonic Impact Treatment,” Applied Ultrasonics, Vol. 44, pp. e533- e538, 2006. [19] K.P. Donnelly and B.R. Varlow, “Nonlinear DC and A.C. Conductivity in Electrically Insulating Composites,” Dielectrics and Electrical Insulation, Vol. 10, pp. 610-614, 2003. | ||
|