Estimation of Fatigue Deformation for Polyetheretherketone (PEEK) and Cast Cobalt-Chromium Circumferential Clasps: A comparative study | ||
| Al-Rafidain Dental Journal | ||
| Article 4, Volume 22, Issue 1, 2022, Pages 28-35 PDF (630.22 K) | ||
| Document Type: Research Paper | ||
| DOI: 10.33899/rdenj.2021.129387.1083 | ||
| Authors | ||
| Hussain Talal Abed* ; Aliaa W. Al-Omari | ||
| Prosthodotic, university of mosul, ninavah, Iraq | ||
| Abstract | ||
| Aims: This in-vitro study aimed to compare the fatigue deformation of Polyetheretherketone (PEEK) and Cobalt-Chromium (Co-Cr) clasps by mechanical cycling test simulating ten years of use. Materials and Methods: 72 clasps samples were fabricated on a standardized e-max upper right first premolar; it is divided into 24 Co-Cr clasps, and 48 PEEK clasps which were subdivided into two halves (2.4, and 3.00) mm width respectively. Each group was further subdivided (n=8 clasps) according to the amounts of abutment undercut (0.25, 0.50, and 0.75) mm respectively. Each clasp was digitally pictured by a microscope before cycling, and then mechanically cycled by a specifically designed insertion-removal apparatus for 15000 times on its specific abutment crown, and at the end of 15000 cycles, each clasp was digitally re-pictured, and the distance between the clasp tips in millimeter of the pre and post cycling pictures were measured with specific analyzing computer program. Results: The fatigue deformation of Co-Cr clasps was higher significantly than the PEEK clasps for the three undercuts. Deeper undercuts showed a significantly higher fatigue deformation for Co-Cr clasps but not significant for PEEK clasps. Conclusion: The fatigue deformation of PEEK clasps with both widths after 15000 cycles of insertion/removal was lower than Co-Cr clasps fatigue deformation. | ||
| Keywords | ||
| Key words: Polyetheretherketone; cobalt-chroium; clasp; fatigue deformation | ||
|
Statistics Article View: 392 PDF Download: 357 |
||