Ceramic Bond Strength of Various Metal Substrate Using Traditional and Digital Methods | ||
| Tikrit Journal for Dental Sciences | ||
| Volume 10, Issue 2, December 2022, Pages 97-108 PDF (722.12 K) | ||
| DOI: 10.25130/tjds.10.2.1 | ||
| Authors | ||
| Rafal kareem Rasheed; Nidhal Sahib Mansoor | ||
| Department of Prosthetic Dental Technology, College of Health and Middle Techniques,Meddle Technical University, Baghdad, Iraq | ||
| Abstract | ||
| Purpose: The aim of this study was to investigate the bond strength of cobalt-chromium (Co-Cr) metal frameworks prepared with three different production techniques with dental porcelain. Methods: In this study, a total of thirty disc samples divided to Three groups (n = 10/group) of metal cylinders (10 mm diameter x 4mm thickness with ring base (12 mm diameter x 1mm thickness) were fabricated by casting (Co–Cr), CAD CAM milling blank(Co–Cr) and by selective laser sintering SLM (Co–Cr) and abraded with airborne-particles then feldespathic porcelain was applied for all discs (10mm diameter x 2mm thickness), before the shear bond strength (SBS) test, the Surface characteristics of the dental alloys were observed by scanning electron microscopy (SEM) to determine the thickness of the oxide layer then surface roughness tester using TR220 portable roughness tester The average surface roughness (Ra) was determined for each group. SBS test-values and failure modes were recorded. Data were analyzed using ANOVA, Tukey’s HSD (a = 0.05). Result: no statistically significant difference of the metal-ceramic bond strength of the test roughness used between casting, milling, and laser no statistically significant difference of the metal-ceramic bond strength of the SBS test between casting compare with milling, and laser groups SBS test statistically significant difference of the metal-ceramic bond strength of the test between milling, and laser technique. The mode of failure shows was mainly cohesive and mixed for all specimens. Conclusion: Within the scope of this research, the CAD/CAM milling Co-Cr alloy has a shear bond strength comparable to the castable alloy. For metal-ceramic restorations, the CAD/CAM milling Co-Cr alloy is an alternative to the castable alloy. Co-Cr restorations can benefit from CAD/CAM manufacture. | ||
| Keywords | ||
| Co; Cr alloy dental ceramic metal substrate | ||
|
Statistics Article View: 367 PDF Download: 121 |
||