The Effect Of Root Canal Irrigants On The Push –out Bond Strength Of Biodentine | ||
| Tikrit Journal for Dental Sciences | ||
| Volume 3, Issue 2, December 2015, Pages 69-75 PDF (506.92 K) | ||
| DOI: 10.25130/tjds.2015.1.9 | ||
| Author | ||
| Maha M. Yahya (BDS. MSc) Lect.. | ||
| (1 Department of Conservative Dentistry. College of Dentistry. Mosul University, Mosul, Iraq. | ||
| Abstract | ||
| Aims: The aim of This study was to evaluate the effect of some endodontic irrigants on the push-out bond strength Biodentine in comparison with Mineral trioxide aggregate (MTA) and Glass ionomer cement (GIC).Materials and Methods: Mid root dentine of single rooted teeth was horizontally sectioned into 1-mm-thick slices. The canal space of each dentine slice was enlarged with a diamond bur to 1.4 mm in diameter. The samples were divided into 3 groups (n=21)for each, and the following materials were placed, respectively: Biodentine( Septodont, Saint Maur des Foss'es, France),MTA(Dentsply, TulsaDental, Tulsa, OK),and GIC(Medifil, PROMEDICA, Germany).The samples were wrapped in wet gauze for 30 minutes to ensure setting of the materials and then divided into 3 subgroups (n=7)for each, to be immersed into QMix ((Dentsply Tulsa Dental, Tulsa, OK, USA), Bio Pure MTAD (Dentsply Tulsa Dental),and saline solutions for 30 minutes. No irrigant was placed over any test material in the other three subgroups. After incubation for 48 hours, the dislodgement resistance of the samples was measured (with and with exposure to the irrigant solutions) using a universal testing machine. Then the samples were examined under stereomicroscope to determine the nature of the bond failures. Results: The lowest push-out bond strength was observed in the MTA group. Biodentine displayed a significantly higher resistance to displacement than the MTA group. Exposure to QMix, MTAD, and saline solutions did not affect the resistance to displacement of the Biodentine and GIC groups, whereas MTA lost strength after exposure to the irrigant solutions ,but the difference was not significant. Conclusions: The PBS of Biodentine and GIC was not affected by the irrigant solutions. Contact with the irrigant solutions did not have a significant effect on the failure modes of the tested materials. | ||
| Keywords | ||
| wordsBiodentine push out MTAD QMix | ||
|