Improvement of Locally Produced Low- Density Polyethylene | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 26, Issue 9, 2008, Pages 1061-1067 PDF (354.58 K) | ||
| DOI: 10.30684/etj.26.9.2 | ||
| Authors | ||
| Najat .J.saleh; Zanaib Y.shnean | ||
| Dep. of Chemical Engineering, University of Technology-Iraq | ||
| Abstract | ||
| In the present work, a polymer composite was fabricated by mixing LDPE with different wt% of pigment (Fe2O3 and TiO2) to obtain desirable properties in fabrication single screw-extruder was utilized , this mixing machine operated at a temperature between (150-170)Co.some of mechanical properties, such as tensile, impact, hardness and bending test were determined at different weight fraction of composite materials. It was found that the addition of pigment (TiO2 and Fe2O3) to the LDPE leads to increase the modulus of elasticity, tensile strength, tensile strength at break, shore hardness on other hand it decreases the % elongation at break, and for the impact strength. | ||
| Keywords | ||
| Ldpe; Weathering; TiO | ||
|