Study of The Mechanical Properties For Particulate Polymer Blend Composite | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 29, Issue 2, 2011, Pages 76-85 PDF (459.58 K) | ||
| DOI: 10.30684/etj.29.2.19 | ||
| Authors | ||
| بلقيس محمد ضياء; احمد ستار جبار | ||
| Abstract | ||
| This research involves using epoxy resin and (Nitride Butadiene Rubber NBR) to form a blend with different resin ratios (90 – 10)%, (80 – 20)%, (70 – 30)%, and (60 – 40)% to achieve better ratio for impact strength as a function of better toughness; then reinforced with SiO2 and Al2O3 powders with (20%) volume fraction. Mechanical properties were studied including impact strength, wear resistance, and hardness before and after immersion in water and HCl (0.5N). Results showed that the composite (epoxy+NBR+SiO2) had better properties compared with blend and Al2O3 composite. Also the acid solution had affected then properties more than water. All impact and wear and hardness decreased after immersing in solution. | ||
| Keywords | ||
| NBR; polymer blend; wear; impact | ||
|