Influence of Heat Treatment on Hardness And Microstructure of High Chromium Iron Alloy | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 28, Issue 6, 2010, Pages 217-228 PDF (889.8 K) | ||
| DOI: 10.30684/etj.28.6.19 | ||
| Authors | ||
| خضير جاسم محمد; هويده ابراهيم احمد | ||
| Abstract | ||
| This work deals with production of different sizes of grinding balls from high- Cr-iron alloy . Cr contents range between (14-16) wt% carbon content (2.1- 2.4)wt% and Mo content (0.3-0.4)wt% ,those balls used in grinding cement and the materials used in its manufacturing . Many heat treatments had been done on the balls to show thier effects on hardness and microstructure. Balls of (70,80)mm diameters were used in this work. The results show that after heating to (1000)c° holding (90) minutes blast air cooling for given time and cold water quenched, tempering at (400)c° for (4) hrs, still air cooling gave the best results in hardness values with low retained austenite , And nearly the same results could be achieved by oil quenching and the same tempering conditions. | ||
|