Filler Content Effects on the Ultrasonic Response of Composite Materials Using the Pulse-Echo Amplitude Technique | ||
| Journal of Engineering and Sustainable Development | ||
| Article 1, Volume 11, Issue 1, 2007, Pages 29-44 | ||
| Authors | ||
| Amer Yahya Al-Jarjees; Awad Hallosh Khidhir | ||
| Abstract | ||
| The aim of this study is to investigate of the capability of ultrasonic technique in assessment of the filler content effects in polymer matrix composite and to provide additional data concerning the particulars of the use ultrasonic response, velocity and attenuation measurements for quality control and sorting composite materials. For the experiments, filled acrylic (matrix) with different weight percentages of calcium silicate and carbon black powder (fillers) individually were moulded. The pulse-echo amplitude technique and normal probes of (1, 2 & 4 MHz) was used. The directional dependence of velocity, attenuation, hardness and filler content were investigated. Also the ultrasonic measurements were carried out at various testing frequencies to observe the reliability of the technique employed. Both filler type and filler weight (%) were systematically varied to investigate their effects on the ultrasonic response of thermoplastic acrylic (PMMA). It was observed that, in general, as the filler weight (%) increased, there is decay in the ultrasonic response provided particles dispersion and deagglomeration was maintained. Increase of filler weight (%) also accompanied by increase in the ultrasonic attenuation and reduction in ultrasonic velocity and hardness. Clear correlation between these measurements was obtained beyond (15%) filler weight percent. It was concluded that ultrasonic technique are sensitive to the filler content in composite materials. Because the ultrasonic response, attenuation and velocity is dependent upon filler content, and can be used to predict the mechanical properties of the filled composite materials. It can be utilized also to sort composite materials with marked differences in one of the above variables. Furthermore the ultrasonic techniques eliminate the need for preparation and destructive testing of products, which can be carried out in a few minutes, and low cost | ||
|