Cryogenic Treatments of Hot Work Tool Steel (56NiCrMoV7) | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 29, Issue 4, 2011, Pages 750-769 PDF (735 K) | ||
| DOI: 10.30684/ etj.29.4.10 | ||
| Authors | ||
| Amin. D. Thamir1; Ibrahim K. Ahamed2 | ||
| 1Production and Metallurgy Engineering Department, University of Technology/ Baghdad | ||
| 2*Production and Metallurgy Engineering Department, University of Technology/ Baghdad | ||
| Abstract | ||
| The main objective of this paper is to study the effect of Cryogenic treatment of hot work tool steel type (56NiCrMoV7) on the microstructure and mechanical properties. Three different temperature (-50°C,-100°C & -150°C) were selected at different soaking time(1hr,2hr & 3hr) respectively. All cryogenic treatments were adopted after hardening by air & oil respectively. It was concluded that the property enhancement for this tool steel can be attributed by conversion most of retained austenite to martensite accompanied with higher dislocations density that leads to the precipitation of fine carbide during the cryogenic treatment especially at the samples quenched by oil & treated at (- 150°C) with soaking 1hr | ||
|
Statistics Article View: 250 PDF Download: 157 |
||