ALUMINIDE COATING BEHAVIOR OF AIS1330 STAINLESS STEEL | ||
| AL-TAQANI | ||
| Article 1, Volume 21, Issue 4, 2008, Pages 72-83 | ||
| Authors | ||
| George M. Hannoush; Ahmed M. Mosa | ||
| Abstract | ||
| AISI330 stainless steel specimens, were coated by pack-cementation aluminization, using single step-high activity process at 1000° C ; for 3,5, and 7hours. The plain aluminide specimens were then heat-treated for 5, and 50 hours at 1000°C. The three types: uncoated, plain aluminide, and plain aluminide then heat treated specimens, were studied under cyclic oxidation at 1000°C for 240 hours in air. The results reveal that best results are obtained for 7 hours plain aluminide then heat treated for 50 hours specimen as compared to other specimens. | ||
|