Effect of Quenching on the forming limit diagram of Aluminum alloy sheets(2024 T3) | ||
| Al-Rafidain Engineering Journal (AREJ) | ||
| Article 4, Volume 17, Issue 1, 2009, Pages 22-33 PDF (0 K) | ||
| DOI: 10.33899/rengj.2009.38618 | ||
| Authors | ||
| T. F. Sultan; W. J. Ali | ||
| Abstract | ||
| Quenching is known as the most critical step in the sequence of heat-treating operations. The objective of quenching is to preserve the solid solution formed at the solution heat-treating temperature, by rapidly cooling to some lower temperature, usually near room temperature. The scope of this study is to construct the forming limit diagram experimentally for aluminum alloy (2024-T3) sheet, as received and after Quenching from solid solution temperature. The results which have been obtained experimentally showed that at (6 hours) after Quenching, there is a considerable effect on the FLC, Quenching increases the FLC at the as received condition in the range of (19-31 %) . الكلمات الدالة: مخطط حد التشكيل ، الإخماد، المعاملة الحرارية المحلولية . | ||
|
Statistics Article View: 426 PDF Download: 305 |
||