Effect of Adding (Binder-Plastisizer-Lubricat) on the Physical Properties of Kaolin | ||
| Baghdad Science Journal | ||
| Article 1, Volume 4, Issue 3, 2007, Pages 397-406 | ||
| Author | ||
| Fadial A. Rasin | ||
| Abstract | ||
| The study concern with the preparation of three type of mixtures; which are prepared from different percentage of polyvenil Butyral, Di-n-butyl phathalate and paraffin wax pastillated. The solvent used is Xylolzul analyses. After washing, Drying and milling the kaolin Dukhla, as a matrix in this study, and by using sieving Tech. The range of particle size used is less than and less than as a mesh batch. The added percentage from prepared mixture were 5% and 10% to 95% and 90% of the matrix respectively. Then disk samples were prepared by using a compaction pressure with heating. After cooling and drying the samples were undergo heat treatment in the range of (1250 – 1350) oC. The measurement of shrinkage and Dielectric properties shows that the satisfied data to be compatible with the industrial properties were for 5% (75%B + 15%P + 10%L) added to 5% to 95% of Kaolin (Particle size less than ); which was fired at 1300oC. | ||
|