Enameling And Study Corrosion Behavior To Low Carbon Steel | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 28, Issue 24, 2010, Pages 6903-6914 PDF (138.35 K) | ||
| DOI: 10.30684/etj.28.24.6 | ||
| Author | ||
| Ali Mezher Resen | ||
| Abstract | ||
| This study includes enameling and study corrosion behavior of low carbon steel (carbon continent =0.11%) in different types of corrosive media like the H2SO4, HCL and NaOH both acidic solution (H2SO4, HCL) has PH= 2 with resistance acid solution enameling and alkaline solution (NaOH) have PH= 12 with resistance alkaline solution enameling. enameling process includes preparing and applying of frit by ground coat method. The corrosion rate calculated using weight loss method at temperature range (30, 40, 60, 90)oC for acidic and (30, 40, 50, 60) oC for alkaline solution. The results indicate that corrosion rate increase with time and temperature for both H2SO4 and HCL solution, while corrosion rate for NaOH solution decreases with time due to the formation of unsolvable compounds on sample surface. These compounds may caused insulation laminar reduced corrosion rate, while corrosion rate increases with temperature because distortion of this layer. | ||
|