Thermal and Electrical Properties of Silica-Mullite-Grqphite Composite Fired at Low Temperature | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 27, Issue 15, 2009, Pages 2835-2843 PDF (216.27 K) | ||
| DOI: 10.30684/etj.27.15.11 | ||
| Author | ||
| Mohsin E. Aldokheily | ||
| Abstract | ||
| Silica - mullite powder sieved through 100 mesh, mixed with graphite at certain proportions and placed in a steel mould, then subjected to ≈ 40Mpa .After air- drying for 24 hours the specimen buried in carbon and fired at 1150 ◦C overnight. DC resistance was measured by the method of two probes. The percolation threshold was not sharp , instead it starts from 10.5% graphite ratio up to 21% were it resembles the conductivity of graphite alone . Resistance and reactance analysis were carried out at three frequencies (0.55, 1.5, 5.0) kHz. The specimen was subjected to heating/cooling cycle and the change in DC resistance value (TCR) was found to be less than 1%for each 100◦C rise in temperature | ||
|