THE QUANTITATIVE STRUCTURAL ,QUALITATIVE AND ELECTRICAL PROPERTIES OF (BI2-YTLXBA2-YSRYCA2CU3O10+) SUPERCONDUCTORS

SH. MAHMOOD, AMIR

doi:10.37652/juaps.2011.44295

	THE QUANTITATIVE STRUCTURAL ,QUALITATIVE AND ELECTRICAL PROPERTIES OF (BI2-YTLXBA2-YSRYCA2CU3O10+) SUPERCONDUCTORS
Journal of University of Anbar for Pure Science
Article 26, Volume 5, Issue 3, 2011, Pages 115-120 PDF (1.32 M)
Document Type: Research Paper
DOI: 10.37652/juaps.2011.44295
Author
AMIR SH. MAHMOOD^*
Tikrit University / College of Education
Abstract
This study included preparing samples of the compound (Bi2Ba2Ca2Cu3O10+δ) by the reaction of the solid state under a hydrostatic pressure 8ton/cm2 and annealing temperature 850Co . These are the best circumstances to obtain samples of the mentioned superconductivity compound at high temperatures. The study demonstrated the X-rays diffraction for the compound (Bi2Ba2Ca2Cu3O10+δ ) prepared at annealing temperature 850Co and pressure 9ton/cm2 . The study showed that it has Tetragonal type of crystal structure. At partial substitution for the component TL in Bi, and Sr component in Ba simultaneously, the compound becomes (Bi2-yTlxBa2- ySryCa2Cu3O10+δ) with (X,Y) values equal to (X = 0.05, Y= 0.1, 0.2, 0.3). The study of the crystal structure test showed that the structure retains on the tetragonal type, and the critical temperature Tc steps-up from (132k) to (138k) at substitution rate (X= 0.05, Y= 0.1). But at increasing the substitution rate for (Y) and the stability of (X) rate more than (X= 0.05, Y= 0.1), the temperature declines to (125k). Finally, The crystal structure of the samples has been studies and tested by Scanning Electron Microscope; knowing the components' rates in the compound; how the annealing temperature and the imposed pressure affect the compound; how the compound partial substitution affect in the components; and specifying the quantitative and qualitative rates of the components in the compound
Keywords
yTlxBa; ySryCa

References
الجمال , یحیى نوری," فیزیاء الحالة الصلبة", دار الکتب للطباعة والنشر, جامعة الموصل ,(1990) . Hag A. U. " The Advant of Higher Temperature Super Conducting Materials ", Science Technology and Development V. 7,3,(1988) الراوی , صبحی سعید, شاکر جابرب شاکر, یوسف مولود حسن, "فیزیاء الحالة الصلبة" , دار الکتب للطباعة والنشر, جامعة الموصل , (1989) الشاذلی , عبد الفتاح ," فیزیاء الجوامد", الدار العربیة للنشر والتوزیع , (2003). Gautreau R., Sarin W. ,"Modern Phyics", Mc Graw-Hill Companies, (1999). Omar M. A., "Elementary Solid State Physic Priciples and Applications ", Addesion- Wesley , (1975). Maxwell E., 'Phys. Rev.',V.78,P.477,(1950). Kittel C.," Introduction to Solid State Physics", 8th ed., John Wiley and Sons, Inc, (2005). Rohlf, "Superconductivity Concepts", Hyper Physics R. Nave, Georgia Stat University, (2005). Lynn J. W., " High Temperature Superconductivity ", Springer-Verlag , (1990). Bahoum S.A., M.Sc., Thesis University if Scince and Technology , Jordan , December, (2005). Tarascon J. M., Barbonx P.,, Greene L. H., Bagley B. G., 'Physica C', V.566, P.153-155 ,(1988). Kadham A. M., Ali A. D., 'Sept. of Phys.', No.13,P.13,(2000). Ginsberg D. M., "Physical Propertise of HTSC(I)", By Marker J. T., Dalichaouch Y. and Maple M. B., World Scientific, (1989). Sehilling A., Halliger E. 'physica', V.157,P. 144, (1989). Ali, Abdul-Kareem D., Ph.D. thesis, Mosul University, Feb. 2007. Kadham A. M., Ali A. D., 'Sept. of Phys.', No.15,P.23,(2002).