Characterization and Cracking Activity of Zeolite Prepared from Local Kaolin | ||
| Iraqi Journal of Chemical and Petroleum Engineering | ||
| Article 1, Volume 11, Issue 2, 2010, Pages 35-42 | ||
| Authors | ||
| Ameel M. Rahman; Samar Karim; Abdul Halim A.K. Mohammed | ||
| Abstract | ||
| The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor at duration time in the range 10-240 minutes, temperature 823 K, and LHSV 1 h-1. The prepared and the standard catalysts were characterized by atomic absorption, X-Ray Diffraction Analysis, Fourier Transform Infrared Spectroscopy, surface area and pore volume. | ||
|