Influence of Simultaneous Doping of Tl on the Transition Temperature Tc and the Lattice Parameters of HgBa2Ca2Cu3O8+ δ Superconductors | ||
| Ibn Al-Haitham Journal For Pure And Applied Science | ||
| Article 1, Volume 22, Issue 3, 2009, Pages 86-82 | ||
| Author | ||
| K. A. Jassim | ||
| Abstract | ||
| In the present study, we have reported investigations on the effect of simultaneous substitution of Tl at the Hg site in the oxygen deficient HgOδ layer of Hg1-xTlxBa2Ca2Cu3O8+ δ cuprate superconductor. Bulk polycrystalline samples were prepared by the two-step solid state reaction process. It was observed that the grown Hg1-xTlxBa2Ca2Cu3O8+ δ corresponds to the 1223 phase. Electrical resistivity, using four probe technique, is used to find the transition temperature Tc. The highest Tc(0ffset) were 108, 102,113, 118, 125 and 121K for Hg1-xTlxBa2Ca2Cu3O8+ δ with x = 0.0, 0.05, 0.10, 0.15, 0.20 and 0.25 respectively. The optimum Tc(off) of ~ 125 K and Tc(onset) ~ 136K was found for the composition Hg0.80Tl0.20Ba2Ca2Cu3O8.293. All the samples preparation with O2 flow, we found that the O2 flow in our samples produce high- Phase superconductors. X-ray diffraction(XRD) analysis showed a pseudotetragonal structure with an increase of the c-axis lattice constant for the samples doped with Tl as compared with these have no Tl content. It was found that the change of the Tl concentrations of all our samples produces a change in the Mass density ρm, c/a and volume fraction VPh(1223). | ||
|