Effects of CaO–B2O3 Glass on Sintering and Microwave Properties of Cordierite Ceramics for Low-Temperature Cofired | ||
| Iraqi Journal of Applied Physics Letters | ||
| Article 1, Volume 1, Issue 1, 2008, Pages 16-20 | ||
| Authors | ||
| A.M. Jasim; H.J. Hameed | ||
| Abstract | ||
| The densification behavior and dielectric properties of cordierite ceramics adding three different proportions of CaO–B2O3 glass were investigated. The cordierite ceramics were prepared from the waste of porous ceramics. Their crystalline phases, densification parameters, dielectric properties, and microstructure were addressed. The densities of all samples firstly increased and then decreased. The crystalline phase of samples was cordierite. It was considered that CaO–B2O3 glass and cordierite ceramic did not react in the process of sintering. With 10, 15, 20 wt% CaO–B2O3 glass added, the maximal densities of samples were 2.46, 2.42, and 2.33 g/cm3, respectively, obtained at 1060, 1000, and 940°C. The materials had a low dielectric constant and a low dielectric loss [~5, tan ~(2-3) x10-3, at about 10GHz]. The sample, with 15wt% CaO–B2O3 glass added, sintered at 1020°C (binder burning temperature at 500°C, with a heating rate of 3°C/min) had better properties (~5.14, tan=2.23x10-3 at 10.328 GHz). | ||
| Keywords | ||
| Cordierite ceramics; CaO; LTCC; Dielectric properties; Sintering | ||
|