Evaluation Of Future Performance of Northern Fatha Storage System | ||
| Tikrit Journal of Engineering Sciences | ||
| Article 1, Volume 20, Issue 4, 2013, Pages 11-17 PDF (0 K) | ||
| Abstract | ||
| This present study shows ,the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Alumium alloy A380 was studied .From fig(5) its clear that ,the microstructure of prepare casting samples consist of two phases hard eutectic (Al-Si) and Primary α-Al.The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84)MP | ||
| Keywords | ||
| The Study of Effect of Applied Pressure on Microstructure and Actual Density for A | ||
|