The Effect of Tool Geometry for Resistance Spot Welds on Crack Growthin Specimens of Mild Steel | ||
| Engineering and Technology Journal | ||
| Article 3, Volume 31, Issue 12, 2013, Pages 2242-2250 PDF (587.13 K) | ||
| DOI: 10.30684/etj.31.12A.3 | ||
| Author | ||
| Nadhim M.Faleh | ||
| Abstract | ||
| A mechanism of crack growth was investigated in resistance spot welds of mild steel. The experiments in this study were designed to investigate the effects of the electrode cap geometrieson fatigue life of the resistance spot weld specimens. Two types of electrode cap geometries were used. These types are 4.8 mm and 6.3 mm nose,used with the same shank in welding operations of 2mm mild steel plate. To obtain the goal, operating factors were precisely controlled, especially the electrode force and welding current of spot welds, to keep the same operating conditions while changingthe electrode geometries. The life test results showed an improvement in the fatigue life of resistance spot welds. The increment was 30% in heavy loads and 10% in low loads based on tool geometry. The improvement in the fatigue life was produced by reducing the diameter of the nose in the geometry of the tool. | ||
| Keywords | ||
| sistance Spot Welding; fatigue; Crack propagation; Mild Steel | ||
|
Statistics Article View: 275 PDF Download: 162 |
||