Preparation and Characterization of Porous Anodic Alumina membrane | ||
| Engineering and Technology Journal | ||
| Article 1, Volume 31, Issue 16, 2013, Pages 3061-3066 PDF (574.55 K) | ||
| DOI: 10.30684/etj.31.16A.5 | ||
| Authors | ||
| Ahmed. A. Hashoosh; Kahtan. K. Al-Khazraji; Ahmed. A. Moosa | ||
| Abstract | ||
| Porous Anodic Alumina (PAA) was prepared by two-step anodization on both sides of an aluminium foil. The anodization carried out at anodizing temperature 17oC using oxalic acid as an anodizing electrolyte. The (PAA) template was characterized with optical microscope and SEM. The optical microscope image showed two (PAA) layers after the dissolution of the residual aluminium. The average pore diameter was found to be (75) nm. The average interpore distance of (PAA) prepared was found to be (99) nm. The thickness of (PAA) was found to be (59.5) μm. | ||
| Keywords | ||
| Porous Anodic Alumina | ||
|
Statistics Article View: 220 PDF Download: 168 |
||