The Effect of Microwave Disinfection on Tensile Strength of Dental Gypsum

Hasan, Radhwan H

doi:10.33899/rden.2008.9055

	The Effect of Microwave Disinfection on Tensile Strength of Dental Gypsum
Al-Rafidain Dental Journal
Article 12, Volume 8, Issue 2, 2008, Pages 213-218 PDF (0 K)
Document Type: Research Paper
DOI: 10.33899/rden.2008.9055
Author
Radhwan H Hasan
Abstract
Aims: To evaluate the effect of microwave disinfection on diametral tensile strength (DTS) of type III and type IV dental stones. Materials and Methods: A total of 80 cylindrical specimens was prepared with dimensions 40 mm in height and 20 mm in diameter. These specimens were divided into 4 main groups: Geastone type III, Zeta type III, Micromod type IV and Silky Rock type IV. Twenty specimens for each main group were divided into 10 specimens as control subgroup and 10 specimens representing microwave irradiated subgroup. The microwave irradiation was performed in a household microwave oven at 900 watts for 5 minutes. The DTS was conducted on a mechanical testing machine at a cross head speed of 1.0 mm/minute. The data were statistically analyzed using Student's t–test, analysis of variance and Duncan's Multiple Range test. Results: The microwave disinfection caused significant increase in DTS (p < 0.05) for all types of dental stone, and dental stones type IV (Micromod and Silky Rock) had significantly higher DTS (p < 0.05) than dental stones type III (Geastone and Zeta). Conclusion: Microwave disinfection of gypsum cast cause significantly increase in diametral tensile strength of type III and type IV dental stone.
Keywords
microwave disinfection; diametral tensile strength; Stone; dental gypsum