Structural and Electrical Properties Dependence on Annealing Temperature of Bi Thin Films | ||
| Baghdad Science Journal | ||
| Article 1, Volume 11, Issue 3, 2014, Pages 1257-1260 | ||
| Author | ||
| Fatin. G. Hachim | ||
| Abstract | ||
| In this work the effect of annealing temperature on the structure and the electrical properties of Bi thin films was studied, the Bi films were deposited on glass substrates at room temperature by thermal evaporation technique with thickness (0.4 µm) and rate of deposition equal to 6.66Å/sec, all samples are annealed in a vacuum for one hour. The X-ray diffraction analysis shows that the prepared samples are polycrystalline and it exhibits hexagonal structure. The electrical properties of these films were studied with different annealing temperatures, the d.c conductivity for films decreases from 16.42 10-2 at 343K to 10.1110-2 (.cm)-1 at 363K. The electrical activation energies Ea1 and Ea2 increase from 0.031 to 0.049eV and from 0.096 to 0. 162 eV with increasing of annealing temperature from 343K to 363K, respectively. Hall measurements showed that all the films are p-type. | ||
| Keywords | ||
| Electrical Properties of Bi; Structural and Electrical Properties of Bi | ||
|