| The quantity of waste generated during construction and demolition keeps rising annually. Refractory bricks are wastes that have a detrimental effect on the environment. This paper investigates the reuse of refractory brick wastes to create environmentally friendly refractory concrete. To accomplish this goal, two percentages 10 and 25% of alumina cement will be substituted for bauxite powder, and alumina brick as the aggregate will be used instead of the natural aggregates. For each of the six types, a mix of refractory concrete (RFC), 14% water content, and a 1:3 cement/ aggregate ratio. The cast samples were stored at laboratory temperature for a full day while still in their molds. The cast samples were left for (24) hours at laboratory temperature in 100% relative humidity. After that, they were opened and placed in water for 7 days to cure. The specimens were placed in an oven to dry at 110 ℃ for 24 hours after seven days of curing in water. The samples were burned for two hours at temperatures between 1000–1100 ℃ at a rate of 3.33 ℃/min. After that, they were cooled to 25 ℃ before being tested. Then, the cast samples were tested to determine the bulk density, shrinkage, compressive strength, modulus of rupture, and weight change. The produced RFC performed almost comparably to those obtained on conventional RFC. This implies that waste alumina bricks as aggregate, with bauxite powder, can be used to manufacture RFC. |
- M.Khattab, S. Hachemi, M.F. al Ajlouni, Recycled Refractory Brick as Aggregate for Eco-friendly Concrete Production, J. Adv. Sci. Eng. Technol., 4 (2121 ) 32-49. https://doi.org/10.32441/jaset.04.01.04
- V.A. Abyzov, Lightweight Refractory Concrete Based on Aluminum-Magnesium Phosphate Binder, Procedia Eng., 150 (2016) 1440-1445. https://doi.org/10.1016/j.proeng.2016.07.077
- P. Hosseini, E. Eslami, M. Poorjafari, S. Vahidi, A. Madari, The Comparison of Silicate Binder Refractory Concretes with Alumina Binder Concretes, First International and 14th National Studentship Conference on Civil Engineering August, Semnan University, I.R. IRAN,2008. https://civilica.com/doc/64123/
- R. Dickuviene, K. Brinkiene, J. Česniene, A. Makstys, Effect of Fiber and Microsilica Incorporation on High Temperature Resistance of Cementitious Complex Binder, Mate. Sci., 17 (2011)1392–1320. https://doi.org/10.5755/j01.ms.17.1.253
- Newman, J.and Choo, B.S. Advance Concrete Technology, published in UK, Elsevier,2003.
- I. Netinger, I. Kesegic, I. Guljasn, The effect of high temperatures on the mechanical properties of concrete made with different types of aggregates, Fire Safety J., 46 (2011) 425-430. http://dx.doi.org/10.1016/j.firesaf.2011.07.002
- W. Bareiro, F. Silva, E. Sotelino , O. omes, The influence of alumina content on the chemical and mechanical behavior of refractory concrete fired at different temperatures, Constr. Build. Mater., 187 (2018) 1214–1223. https://doi.org/10.1016/j.conbuildmat.2018.08.065
- K. Jadeja , K. Saradava , Property Analysis Of Alumina Refractory Bricks - A Review, Int. J. Futuristic Trends in Eng. Technol., 1 ( 2014) 1-3. https://www.researchgate.net/publication/287993880
- American Concrete Institute, ACI Committee 547-2008, Refractory Concrete. https://www.concrete.org/aboutaci/introductiontoaci.aspx
- American Society for Testing and Materials C860 – 2019, Standard Test Methods for Determining the Consistency of Refractory Castable Using the Ball–In–Hand Test, vol. 15.1. https://www.scribd.com/search?query=Astm%20C860
- American Society for Testing and Materials C862 – 2020, Standard Test Methods for Preparing Refractory Concrete Specimens by Casting, Vol. 15. https://webstore.ansi.org/standards/astm/astmc862162020
- American Society of Testing and Materials C 865-2022, Standard Practice for Firing Refractory Concrete Specimens, Vol. 15.1. https://webstore.ansi.org/search/find?in=1&st=ASTM+C865
- American Society of Testing and Materials C 20-2022,Standard Test Method for Apparent Porosity,Water Absorption, Apparent Specific Gravity,and Bulk Density,Vol.15.1.https://www.scribd.com/document/730910030/ASTM-C20-00-2022
- American Society for Testing and Materials C133 –2021, Standard Test Methods for Cold Crushing Strength and Modulus of Rupture of Refractories, Vol. 15.1. https://standards.globalspec.com/std/14376412/ASTM%20C133-97(2021)
- British Standard Inst: BS 1902: Section 7.6: 1987, Refractory Materials, Testing of Mate. Performed Test Pieces, https://shop.standards.ie/en-ie/standards/bs-1902-7-6-1987-196628_saig_bsi_bsi_468957/
- A. Baradaran-Nasiri, M. Nematzadeh, The effect of elevated temperatures on the mechanical properties of concrete with fine recycled refractory brick aggregate and aluminate cement, Constr. Build. Mater., 147 (2017) 865–875. https://doi.org/10.1016/j.conbuildmat.2017.04.138
- D. Abdullah, Z. Abbas , S. Abed, Some Properties of Concrete Containing Waste Brick As Partial Replacement Of Coarse Aggregate And Addition Of Nano Brick Powder, IOP Conf. Ser. Earth Environ. Sci., 961,2022,012093. http://dx.doi.org/10.1088/1755-1315/961/1/012093
- I. Altun, effect of temperature on the mechanical properties of self-flowing low cement refractory concrete, Cem. Concr. Res., 31 (2001) 1233–1237. https://doi.org/10.1016/S0008-8846(01)00533-6
- V. Letelier, J. Ortega, P. Muñoz, E. Tarela, G. Moriconi, Influence of Waste Brick Powder in the Mechanical Properties of Recycled Aggregate Concrete, Sustainability, 10 (2018) 1037. https://doi.org/10.3390/su10041037
- J. Ortegaa, V. Letelier, C. Solasa, G. Moriconic, M. Climenta, I. Sánchez, Long-term effects of waste brick powder addition in the microstructure and service properties of mortars, Constr. Building Mater., 182 (2018) 691–702. https://doi.org/10.1016/j.conbuildmat.2018.06.161
- M. Hiremath, S. Sanjay , D. Poornima, Replacement of Coarse Aggregate by Demolished Brick Waste in Concrete, Int. J. Sci. Technol. Eng., 4 ( 2017) 2349-784X. https://www.ijste.org/articles/IJSTEV4I2029.pdf
- F. Kallak, Use of Crushed Bricks as Coarse Aggregate in Concrete, Tikrit J. Eng. Sci., 16 (2009) 64-69. https://tj-es.com/wp-content/uploads/2018/07/vol16no3p6.pdf
- S. Zhang, L. Zong, Properties of Concrete Made with Recycled Coarse Aggregate from Waste Bric, Environ. Prog. Sustain. Energy, 33 (2014) 1283-1289. https://aiche.onlinelibrary.wiley.com/doi/abs/10.1002/ep.11880
- H. Khan, A. Castel, M. Khan, A. Mahmood, Durability of calcium aluminate and sulphate resistant Portland cement based mortars in aggressive sewer environment and sulphuric acid, Cem. Concr. Res., 124 (2019) 105852. https://doi.org/10.1016/j.cemconres.2019.105852
|