J. Salaman, A., A. Mahmood, A., I. Al-Mosawi, A., A.Alwash, N. (2011). Using of Coating Technique by Inorganic Flame Retardants to Protect Civil and Industrial Foundations from Fires. , 7(4), 97-102.
Ali J. Salaman; Abbas A. Mahmood; Ali I. Al-Mosawi; Naser A.Alwash. "Using of Coating Technique by Inorganic Flame Retardants to Protect Civil and Industrial Foundations from Fires". , 7, 4, 2011, 97-102.
J. Salaman, A., A. Mahmood, A., I. Al-Mosawi, A., A.Alwash, N. (2011). 'Using of Coating Technique by Inorganic Flame Retardants to Protect Civil and Industrial Foundations from Fires', , 7(4), pp. 97-102.
J. Salaman, A., A. Mahmood, A., I. Al-Mosawi, A., A.Alwash, N. Using of Coating Technique by Inorganic Flame Retardants to Protect Civil and Industrial Foundations from Fires. , 2011; 7(4): 97-102.

Using of Coating Technique by Inorganic Flame Retardants to Protect Civil and Industrial Foundations from Fires

Al-Khwarizmi Engineering Journal
Article 1, Volume 7, Issue 4, 2011, Pages 97-102
Authors
Ali J. Salaman; Abbas A. Mahmood; Ali I. Al-Mosawi; Naser A.Alwash
Abstract
تم في هذا البحث زيادة إعاقة اللّهب لأجزاء المنشآت المدنية والصناعية المصنعة من المواد المتراكبة البولميرية المتقدمة المقواة بالألياف بطلائها بطبقة سطحية مكونة من مادة معيقة للّهب . إستعمل رابع أُوكسيد الأنتيمون كطبقة طلاء بسمك (3mm) لإعاقة اللّهب ومنع إنتشاره لطلاء سطح راتنج البولي أستر (SIROPOL 8340-PI) المقوى بألياف هجينة مكونة من حصيرة ألياف الكاربون وألياف كيفلار(49) (º 0 -º 45) ، وتعريضها إلى لهب مباشر متولد من شُعلة غازية درجة حرارتها (2000ºC) وبمسافات تعرض مختلفة(20mm,15,10) ودراسة مدى مقاومة هذه الطبقة للحرارة ومدى قدرتها على حماية المادة المتراكبة التي تحتها .لقد أظهرت النتائج العملية التي تم التوصل إليها من إختبار التعرية الحرارية تحسن مقاومة المادة المتراكبة للحرارة العالية بعد إضافة طبقة رابع أُوكسيد الأنتيمون وتزداد هذه المقاومة مع زيادة مسافة التعرض لحرارة اللّهب .